OCr21AI4 (214),FCHW-2,The Spring Type Heat Wire of Fecral Heating Wire in Furnace

Sep 01, 2016

Basic Info.

Model NO.:OCr21AI4Product Type:Strip
Material:Fecral AlloyCarbon Content:Low Carbon
Package:Waterproof Film, PalletSpecification:CE, RoHS
Trademark:UALLOYOrigin:China
Wire:0.018mm-10mmRibbon:0.05*0.2mm-2.0*6.0mm
HS Code:7220900000Production Capacity:5000 Tons/Year

Product Description


OCr21AI4 (214), FCHW-2,  The Spring Type Heat Wire Of  FeCrAl Heating Wire in Furnace
 
0Cr21Al4
General Information
FeCrAl, a family of iron-chromium-aluminum alloys (Kanthal APM, A-1, D and AF etc.) used in a wide range of resistance and high-temperature applications is also used in the form of resistance wires.
Name:heating  wire
colour:oxidized  or  shining 
Package: Carton or wooden case as demanded
Application: making heating equipment like industrial furnace, civil heating appliance, various electrical resistors and locomotive braking resistor
Place of Origin: Jiangsu, China (Mainland)
 


Designation
Components






NiFeZnMnCuAICrSi
NCHW-177 Min  2.5 Max  19~210.75~1.5
NCHW-257 Min  1.5 Max  15~180.75~1.5
FCHW-1 rem 1.0 Max 4.0~6.023~261.5 Min
FCHW-2 rem 1.0 Max 2.0~4.017~221.5 Min



Usage: Resistor 

Size: Thickness 0.01-7mm, width 1mm-1000mm

Surface: BA, 2B
 


Alloy material

Chemical composition %










C

P

S

Mn

Si

Cr

Ni

Al

Fe

others


max(≤)











Cr20Ni80

0.08

0.02

0.015

0.6

0.75-1.60

20.0-23.0

Rest

≤0.50

≤1.0

-

Cr30Ni70

0.08

0.02

0.015

0.6

0.75-1.60

28.0-31.0

Rest

≤0.50

≤1.0

-

Cr15Ni60

0.08

0.02

0.015

0.6

0.75-1.60

15.0-17.0

55.0- 61.0

≤0.50

Rest

-

Cr20Ni35

0.08

0.02

0.015

1

1.00-3.00

18.0-21.0

34.5-36.0

-

Rest

-

Cr20Ni30

0.08

0.02

0.015

1

1.00-2.00

18.0-21.0

30.0-31.5

-

Rest

-

1Cr13Al4

0.12

0.025

0.025

0.7

≤1.00

12.5-15.0

-

3.5-4.5

Rest

-

0Cr15Al5

0.12

0.025

0.025

0.7

≤1.00

14.5-15.5

-

4.5-5.3

Rest

-

0Cr25Al5

0.06

0.025

0.025

0.7

≤0.60

23.0-26.0

≤0.60

4.5-6.5

Rest

-

0Cr23Al5

0.06

0.025

0.025

0.7

≤0.60

20.5-23.5

≤0.60

4.2-5.3

Rest

-

0Cr21Al6

0.06

0.025

0.025

0.7

≤1.00

19.0-22.0

≤0.60

5.0-7.0

Rest

-

1Cr20Al3

0.06

0.025

0.025

0.7

≤1.00

18.0-21.0

≤0.60

3.0-4.2

Rest

-

0Cr21Al6Nb

0.05

0.025

0.025

0.7

≤0.60

21.0-23.0

≤0.60

5.0-7.0

Rest

Nb add0.5

0Cr27Al7Mo2

0.05

0.025

0.025

0.2

≤0.40

26.5-27.8

≤0.60

6.0-7.0

Rest

 
 


 
 
in the form of wire, ribbon and strip
 
Wire: 0.018mm-10mm
Ribbon: 0.05*0.2mm-2.0*6.0mm
Strip: 0.5*5.0mm-5.0*250mm
 Packaging & Delivery


Packaging Details:
plastic film inside , wooden pallets outside , choose the suitable packing, it can be customized by the clients' demand.
Delivery Detail:about 5-25 days


 
WHY CHOOSE  US?
 
All our raw material is made from prime material, not recycle material. We have more than 10 years experience in manufacturing resistance heating alloys.
 
In the market, not all the NiCr alloys are with standard chemical composition and stable resistance. Professional and reliable is the soul of our business.
 
1) We achieve consistent production from smelting to complete products, we are able to supply satisfactory products.
 
2) We have has the world's advanced level of German ALD - VIDP1000 - 8000KG vacuum induction furnace and wire drawing machines from Japan.
 
3) With our skilled spooling knowhows, we have successfully magnified the take - up weight on spool. For example, even a superfine wire of 0.04 mm in diameter can be wound and shipped on a 3 - 4 kg bobbin, thus immediately contributing to your productive efficiency.
 
4) In order to prevent a wire from loosening, we have introduced a developed tension controlled systems into our take - up machine and respooling machine. 
 
We think you can anticipate smooth despooling.