Heating resistance alloy manufacturer / supplier in China, offering 0cr25al5 Resistance Strip/Fecral Heating Alloy,NiCr resistance alloy,FeCrAl resistance alloy,CuNi resistance alloy etc in the form of wire and strip. More favourable price from factory,welcome your inquiry.
| Model NO.:0Cr25Al5 | Product Type:Strip |
| Material:Fecral | Carbon Content:Low Carbon |
| Trademark:ualloy | Origin:China |
| HS Code:85149090 |
0Cr25Al5 resistance strip/FeCrAl Heating Alloy
1. Description
With the characteristics of high resistance, low coefficient of electric resistance, High operating temperature, good corrosion resistance under high temperature.
It is mainly used in electric ceramic cooktop, industrial furnace.
2. Specification
1). Electric ceramic cooktop resistance strip:
Thickness: 0.04mm-1.0mm
Width: 5mm-12mm
Thickness&Width: (0.04mm-1.0mm)× 12mm(above)
2). Low resistance ribbon:
Thickness&Width: (0.2mm-1.5mm)*5mm
3). Industrial furnace ribbon:
Thickness: 1.5mm-3.0mm
Width: 10mm-30mm
3. Usage
It is mainly used in electric locomotive, diesel locomotive, metro vehicle and high speed moving car etc brake system brake resistor, electric ceramic cooktop, industrial furnace.
4. Features
Stable performance; Anti-oxidation; Corrosion resistance; High temperature stability; Excellent coil-forming ability; Uniform and beautiful surface condition without spots.
5. Packing detail
1) Coil (plastic spool) + compressed ply-wooden case + pallet
2) Coil (plastic spool) + carton + pallet
6. Products and services
1). Pass: ISO9001 certification, and SO14001cetification;
2). Fine after-sale services;
3). Small order accepted;
4). Stable properties in high temperature;
5). Fast delivery;
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | Other |
| Max | |||||||||
| 0.06 | 0.025 | 0.025 | 0.70 | Max 1.0 | 23.0~26.0 | Max 0.60 | 4.5~6.5 | Bal. | - |
Mechanical Properties
| Max Continuous Service Temp | 1250ºC |
| Resisivity at 20ºC | 1.42 ohm mm2/m |
| Density | 7.10 g/cm3 |
| Thermal Conductivity | 46.1KJ/m@h@ºC |
| Coefficient of Thermal Expansion | 16.0×10-6/ºC |
| Melting Point | 1500ºC |
| Tensile Strength | 637~784 Mpa |
| Elongation | Min 12% |
| Section Variation Shrink Rate | 65~75% |
| Repeatedly Bend Frequency | Min 5 times |
| Continuous Service Time | - |
| Hardness | 200-260HB |
| Micrographic Structure | Ferrite |
| Magnetic Property | Magnetic |